COATING TYPE - Rutile-cellulose

AWS A 5.1:E 6013 ISO 2560-A-E 42 0 RC 11 ГОСТ 9466 - 75

Э 46 –АНО-36--Ø-УД

Е 43 2(3) РЦ 11

ТУ У 05416923.050-99

Electrodes ANO-36 distinguished by easy primary and secondary ignition, arc smoothness and stability, low spatter loss, even coverage melting, excellent forming of weld bead, easy slag removal. With electrodes of small diameter, the welding can be performed from the power sources connected to conventional mains. Easy handling with electrodes makes it possible to perform welding even by a beginning welder. Electrodes are not sensitive to edges quality, rust and other surface contaminations. 

PURPOSE AND FIELD OF APPLICATION

Designed for manual metal arc welding at direct or alternate current of general and critical structures from mild steel according to ДСТУ 2651-2005/ГОСТ 380-2005 (Ст 0, Ст 1, Ст 2, Ст 3) of all groups А, Б, В and all degrees of disoxidation  – "Rimmed" (“КП”), "Semi-killed" (“ПС”), "Killed" (“СП”) and ГОСТ 1050-88 (05кп, 08кп, 08пс, 08, 10кп, 10пс, 10, 15кп, 15пс, 15, 20кп, 20пс, 20) in all the spatial positions (except vertical-down for 5,0 mm diameter electrodes).

 

APPLICATION CONDITIONS

Deposition rate factor – 7,8-8,0 g g/A.hr. Electrode consumption per 1 kg of deposited metal is 1,68 kg.

REDRYING BEFORE WELDING

At the normal storage conditions, the electrode baking is not required. In case of moisture, the baking is made at 110±10°С for 25-30 min.

 

 

CHEMICAL COMPOSITION OF DEPOSITED METAL, %

Mn Si C P S
0.40-0.65 0.10-0.35 ≤ 0.11 ≤ 0.035 ≤ 0.030

 

MECHANICAL PROPERTIES OF WELD METAL

Tensile strength, MPa Yield strength, MPa Elongation, %

Impact strength, J / сm²

+20 ˚С

Absorbed striking energy, J

0 ˚С

500-640 ≥ 420 ≥ 22 ≥ 78 ≥  47

Welding should be done with direct current of any polarity (reversed polarity is recommended, “+” is on an electrode) or with AC current from a transformer with open-circuit voltage not less than 50V. 

 

 

PACKAGING DATA

Diameter, mm Length, mm Welding current, А Number of electrodes in package, pcs Weight of packing, kg
3 350 80-120 36-37; 90-93 1; 2.5
4 450 130-180 80-83 5
5 450 170-240 53-54 5

 

WELDING POSITIONS

PA        PB        PC        PF

 

PG      PE      PD

 

ДСТУ EN ISO 6947

 

 