COATING TYPE - Rutile-cellulose
| AWS A 5.1:E 6013 |
ISO 2560-A-E 42 0 RC 11 |
ГОСТ 9466 - 75 |
Э 46 –АНО-36--Ø-УД
Е 43 2(3) РЦ 11
|
ТУ У 05416923.050-99
Electrodes ANO-36 distinguished by easy primary and secondary ignition, arc smoothness and stability, low spatter loss, even coverage melting, excellent forming of weld bead, easy slag removal. With electrodes of small diameter, the welding can be performed from the power sources connected to conventional mains. Easy handling with electrodes makes it possible to perform welding even by a beginning welder. Electrodes are not sensitive to edges quality, rust and other surface contaminations.
PURPOSE AND FIELD OF APPLICATION
Designed for manual metal arc welding at direct or alternate current of general and critical structures from mild steel according to ДСТУ 2651-2005/ГОСТ 380-2005 (Ст 0, Ст 1, Ст 2, Ст 3) of all groups А, Б, В and all degrees of disoxidation – "Rimmed" (“КП”), "Semi-killed" (“ПС”), "Killed" (“СП”) and ГОСТ 1050-88 (05кп, 08кп, 08пс, 08, 10кп, 10пс, 10, 15кп, 15пс, 15, 20кп, 20пс, 20) in all the spatial positions (except vertical-down for 5,0 mm diameter electrodes).
APPLICATION CONDITIONS
Deposition rate factor – 7,8-8,0 g g/A.hr. Electrode consumption per 1 kg of deposited metal is 1,68 kg.
REDRYING BEFORE WELDING
At the normal storage conditions, the electrode baking is not required. In case of moisture, the baking is made at 110±10°С for 25-30 min.
CHEMICAL COMPOSITION OF DEPOSITED METAL, %
| Mn |
Si |
C |
P |
S |
| 0.40-0.65 |
0.10-0.35 |
≤ 0.11 |
≤ 0.035 |
≤ 0.030 |
MECHANICAL PROPERTIES OF WELD METAL
| Tensile strength, MPa |
Yield strength, MPa |
Elongation, % |
Impact strength, J / сm²
+20 ˚С
|
Absorbed striking energy, J
0 ˚С
|
| 500-640 |
≥ 420 |
≥ 22 |
≥ 78 |
≥ 47 |
Welding should be done with direct current of any polarity (reversed polarity is recommended, “+” is on an electrode) or with AC current from a transformer with open-circuit voltage not less than 50V.
PACKAGING DATA
| Diameter, mm |
Length, mm |
Welding current, А |
Number of electrodes in package, pcs |
Weight of packing, kg |
| 3 |
350 |
80-120 |
36-37; 90-93 |
1; 2.5 |
| 4 |
450 |
130-180 |
80-83 |
5 |
| 5 |
450 |
170-240 |
53-54 |
5 |
WELDING POSITIONS
PA PB PC PF
PG PE PD
ДСТУ EN ISO 6947