PURPOSE AND FIELD OF APPLICATION
Monolith R electrodes are designed for manual arc welding conventional and critical structures of low-carbon grades of steels like DC01, DC04, DD13, FeP01, FeP03, 1.0322, 1.0335, St22, USt3, USt4, etc.
APPLICATION CONDITIONS
-designed for welding fillet, butt, overlap joints of metal from 3 up to 20 mm thickness.
- electrodes of diameter 2,0-4,0 mm are good for welding in all positions except “vertical down”; diam. 5mm - for welding in a flat position, in a horizontal position on a vertical surface, and “vertical-up” position.
- welding should be made at DC of any polarity (it is recommended by reverse one, «+» at electrode) or AC from an open-circuit voltage transformer of not less than 50±5 V.
REDRYING BEFORE WELDING
- permissible moisture content in the coating before use is not more than 0.7 %;
- when moistening redrying is required at 120±10ºC / 60 min.
CHEMICAL COMPOSITION OF DEPOSITED METAL, %
Mn |
Si |
C |
P |
S |
0.40-0.65 |
0.10-0.35 |
≤ 0.11 |
≤ 0.035 |
≤ 0.030 |
MECHANICAL PROPERTIES OF WELD METAL
Temporary resistance, MPa |
Yield strength, MPa |
Relative elongation, % |
Impact viscosity KCU +20 ˚С, J / cm²
|
Absorbed striking energy, J 0 ˚С |
500-640 |
≥420 |
≥20 |
≥78 |
≥47 |
Welding should be made at DC of any polarity (it is recommended by reverse one, «+» at electrode) with an arc voltage of 25...30 V or AC from an open-circuit voltage transformer of 50±5 V.
PACKAGING DATA
Diameter, mm |
Length, mm |
Welding current, A |
Units per package, pcs |
Weight of packing, kg |
2 |
300 |
50-70 |
50-53; 100-106 |
0,5; 1,0 |
2.5 |
350 |
70-100 |
53-55; 127-128 |
1,0; 2,5 |
3 |
350 |
80-110 |
36-38; 90-95 |
1,0; 2,5 |
3.2 |
350 |
90-120 |
31-33; 77-78 |
1,0; 2,5 |
4 |
450 |
120-160 |
15-17; 39-42; 81-83 |
1,0; 2,5; 5,0 |
5 |
450 |
150-210 |
53-54 |
5,0 |
WELDING POSITIONS
ДСТУ EN ISO 6947
CERTIFICATION