COATING TYPE - Copper-coated

AWS: A5.18 ER70S-4

ISO 14341-А G 42 4 М21 3Si1

ГОСТ 2246 - 70 CB08ГС-0

ТУ У 25.9-34142621-015:2017

Due to the absence of non-metallic inclusions, the welding-technological properties of deposited material are improved after the plasma vacuum-arc treatment. The application of copper-plated welding wire G3Si1 allows increasing the quality of ready parts and products by forming a clean and reliable weld. 

 

Welding wire G3Si1 guarantees:

- easy arc ignition due to optimal coating and perfect geometric parameters; 

- low spatter loss while welding in CO2 and absence of spatters during welding in gas mixture М21; 

- almost absence of a slag film on weld;

- high stability of arc burning.

 

PURPOSE AND FIELD OF APPLICATION

Welding copper-coated wire G3Si1 is used for automatic and semi-automatic welding of carbon and low-alloy steels with yield strength of up to 420 MPa. The welding wire is widely used for welding pipelines, in ship-building, in automobile and machine building, as well as in construction. The wire is applied in operation with a thick-sheet metal. In this case, the weld is formed for one pass (several passes).

APPLICATION CONDITIONS

Welding copper-coated wire is used for welding (surfacing) of products, parts and structures, made of carbon and low-alloy steels, in flat, vertical and overhead positions. It is possible to perform welding both in gas mixtures, and also in pure CO2. To produce the quality weld, the scale, rust, and different oxide coatings should be removed. During the multi-pass welding, the surface of the previous bead should be cleaned from slag.

 

 

CHEMICAL COMPOSITION OF WIRE, %

C

Si

Mn

Cr

Ni

S

0.06-0.14

0.7-1

1.3-1.6

≤0.15

≤0.15

≤0.15

P

Mo

V

Al

Ti+Zr

Cu

≤0.025

≤0.15

≤0.03

≤0.02

≤0.15

≤0.2

Total content of copper less than 0,35 %.

 

MECHANICAL PROPERTIES OF WELD METAL

Tensile strength, MPa Yield strength, MPa  Elongation, % Impact strength, J-40°C
500-640 ≥20 ≥47 ≥420

 

WELDING CONDITIONS

Nominal diameter of wire, mm Welding current, А  Voltage, V Feed rate, m/hour Protective gas consumption, l/min
0.8 50-150 13-21 260-400 6-8
1 70-200 16-24 160-400 8-10
1.2 90-350 19-34 150-400 8-12
1.6 140-370 17-32 100-350 12-16

Welding should be performed at DC of reverse polarity.

 

 

PACKAGING DATA

Metal spool 

BS 300

Plastic spool 

D 270

Plastic spool 

 

D 200

Plastic spool 

 

D 170

Ø 0,8 mm; Ø 1,0 mm; 

Ø 1,2 mm; Ø 1,6 mm

Ø 0,8 mm; Ø 1,0 mm; 

Ø 1,2 mm

Ø 0,8 mm; Ø 1,0 mm; 

Ø 1,2 mm

Ø 0,8 mm; Ø 1,0 mm

Weight -15 kg / 18 kg 

Weight - 15 kg 

Weight - 5 kg 

Weight – 1 kg /2,5 kg 