COATING TYPE - Basic
ГОСТ 9466 — 75 ГОСТ 9467 — 75 |
Э – 09Х1МФ - ТМЛ-3У-d - ТД Е 16 — Б20 |
ISO: 3580-А-E CrMoV1 B 2 2
A5.5: E8015-G
ТУ У 25.9-34142624-014:2017
COATING TYPE - Basic
ГОСТ 9466 — 75 ГОСТ 9467 — 75 |
Э – 09Х1МФ - ТМЛ-3У-d - ТД Е 16 — Б20 |
ISO: 3580-А-E CrMoV1 B 2 2
A5.5: E8015-G
ТУ У 25.9-34142624-014:2017
PURPOSE AND FIELD OF APPLICATION
Electrodes TML-3U electrodes are designed for manual arc welding with direct current of reverse polarity in all spatial positions, except the vertical down, the equipment and pipelines from steel 12MH, 15ХМ, 20ХМЛ, 12Х2М1, 12Х1МФ, 12Х2МФБ, 12Х2МФСР, 20ХМФЛ, and 15Х1М1ФЛ grades, that operate at a temperature of up to 540 °С.
SPECIAL PROPERTIES
Welding electrodes TML-3U provide metal high resistant to porosity while welding with an elongated arc. Electrodes allow to do narrow cut welding with a common angle of bevel edge not less than 15º. Welding should be done with a short arc on the clean edges.
APPLICATION CONDITIONS
Deposition rate factor: 9,5 g/A.hr. Electrode consumption per 1 kg of deposited metal – 1,5 kg. Designed for welding in all the spatial positions except vertical down.
REDRYING BEFORE WELDING
At the normal storage conditions, the redrying is not required. In case of moisture redrying before welding: 400±20 ºС; 1-1,5 hours. Max 3 times. Moisture content in the coating should not exceed 0,4%.
CHEMICAL CONTENT OF DEPOSITED METAL, %
Mn | Si | C | P | S | Cr | Mo | V |
0.5-0.9 | 0.15-0.40 | ≤0.12 | ≤ 0.030 | ≤ 0.025 | 0.8-1.25 | 0.4-0.7 | 0.1-0.3 |
MECHANICAL PROPERTIES OF WELD METAL
Тимчасовий опір, Н/мм² | Відносне видовження, % | Ударна в’язкість, Дж/см² |
≥490 | ≥16 | ≥78,5 (8) |
Welding should be done with a short arc on the clean edges.
PACKAGING DATA
Diameter, mm | Length, mm | Welding current, A | Units per package, pcs | Weight of packing, kg |
3 | 350 | 80-110 | 92 | 2.5 |
4 | 450 | 110-150 | 82 | 5 |
WELDING POSITIONS
PA PB PC PF
PE PD
ДСТУ EN ISO 6947