COATING TYPE - Basic
ГОСТ 9466 — 75 |
Э– 09Х1МФ - ЦЛ-39 - 2 - ТД Е - 17 — Б20 |
ТУ У 25.9-34142624-014:2017
ОСТ 24.948.01-90
ISO 3580-A- E CrMoV1 B 2 2
AWS A5.5: E8015-G
COATING TYPE - Basic
ГОСТ 9466 — 75 |
Э– 09Х1МФ - ЦЛ-39 - 2 - ТД Е - 17 — Б20 |
ТУ У 25.9-34142624-014:2017
ОСТ 24.948.01-90
ISO 3580-A- E CrMoV1 B 2 2
AWS A5.5: E8015-G
PURPOSE AND FIELD OF APPLICATION
Electrodes RS-39 are designed for manual arc welding with a DC of reverse polarity of heating surfaces of boiler units, as well as root passes seams of thick-walled pipelines joints of heat-resistant steel of the pearlite class 12Х1МФ and 15Х1М1Ф grades, operating at a temperature up to 585 ºС.
SPECIAL PROPERTIES
Welding electrodes RS-39 provide high resistance of a weld metal to the porosity while welding with elongated arc. They allow narrow cut welding with a common angle of bevel edge not less than 15º. The welding seam is durable and resistant to corrosion. Resistant to high temperatures. The low oxidizing capacity of the metal deposited with RS-39 ensures a smooth transition of the alloying metal into the base metal of the product. Thus, the welding seam is heat-resistant and not subject to hot cracks formation. Welding should be made with a short arc; clean the edges before welding.
APPLICATION CONDITIONS
Deposition rate factor: 9,5 g/A.hr. Electrode consumption per 1 kg of deposited metal is 1,6 kg. Designed for welding in all the spatial positions except the vertical down one.
CHEMICAL COMPOSITION OF DEPOSITED METAL, %
С | Mn | Si | Cr | Mo | V | S | P |
≤ 0.12 | 0.6-0.9 | 0.20-0.40 | 0.8-1.25 | ≤ 0.030 | 0,12-1,3 | ≤ 0,025 | ≤ 0,030 |
MECHANICAL PROPERTIES OF WELD METAL
Tensile strength, MPa | Yield strength, MPa | Elongation, % | Impact strength, J/сm² |
≥ 490 | ≥ 343 | ≥16 | ≥78 |
Welding should be done with a short arc on the clean edges.
PACKAGING DATA
Diameter, mm | Length, mm | Welding current, A | Units per package, pcs | Weight of packing, kg |
2.0 | 300 | 60-90 | 56-57 | 1 |
WELDING POSITIONS
PA PB PC PF
PE PD
ДСТУ EN ISO 6947