COATING TYPE — Other

ГОСТ 9466-75 10051-75 Э — 320 X23С2ГТР-HS-Fe15-Ø-НГ
Е 700/59-1-П42

ТУ У 25.9-34142621-013:2016

HS-Fe15 are suitable for welduping of quickwearing surfaces operating in an abrasive environment, and also wherein high hardness is required. Without heat treatment electrodes HS-Fe15 allow to get the less plastic metal bead, but with hardness of HRC 56-63. Such hardness is a result of special alloying elements added in coverage.

PURPOSE AND FIELD OF APPLICATION

Electrodes HS-Fe15 are designed for surfacing parts, operating under conditions of abrasive wear mainly at moderate impact loads. They are applied for surfacing teeth of excavator buckets, operating at the abrasive wear in sandy ground, blades of road machines, plough shares, discs and cultivator blades of agricultural machines, cutting edges of screw conveyors of mixing machines, blades of smoke exhausters, crusher jaws, etc. The mentioned parts, deposited by the electrodes HS-Fe15, possess excellent wear-resistant properties and dependable service characteristics.

APPLICATION CONDITIONS

Deposition rate factor is 9.0 g/А.h. Electrode consumption per 1 kg of deposited metal is 1.4 kg. Before surfacing it is necessary to clean the surface from contaminations, rust, grease. It is not recommended (to avoid crushing) to perform surfacing of steel parts for more than in two layers, while those of cast iron – in one layer. At a large wear of part, the lower layers should be welded with other electrodes, depending on base metal composition. For carbon low-alloy steels a preliminary layer can be deposited by electrodes Monolith RC, Standard RC, while for steels, alloyed with manganese electrodes UONI -13/55 are recommended. The presence of transverse microcracks is not a defect, but an index of high deposition hardness.

REDRYING BEFORE WELDING

At the normal storage conditions, the redrying is not required. In case of moisture redrying is made at 250±10ºС for 60 min. Moisture content in the coating should not exceed 0,5%.

 

CHEMICAL COMPOSITION OF WELD METAL, %

Mn Si C P S Cr Ti B
1.0-1.5 2.0-2.5 2.9-3.5 ≤ 0.040 ≤ 0.035 22.0-24.0 0.5-1.5 0.5-1.5

 

HARDNESS OF DEPOSITED WELD METAL

Hardness, HRС without heat treatment after deposition
56-63

Deposition is carried out in flat and inclined positions with a direct current of reverse polarity with narrow rollers or with small oscillations of the electrode. Also, deposition can be carried out at AC from the transformer with open-circuit voltage (50 ± 5 V).

 PACKAGING DATA

Diameter, mm Length, mm Welding current, A Number of electrodes in package, pc Weight of packing, kg
4 450 130-180 10 1
5 450 170-220 6 0.9

WELDING POSITIONS

PA

ДСТУ EN ISO 6947

 