Welding electrodes Monolith M-Fe6 Ø3 mm: pkg 1 kg

3 мм
1.00 кг
1 package
71.27UAH.
упаковок
71.27 UAH.

COATING TYPE — Rutile basic

DIN 8555: E6-UM-55- G ДСТУ EN 14700 E Z Fe6

Weld metal softening can be performed at 840-860°С with the following hardening to 950-1000°С and cooling in oil or air. Mechanical metal-working acceptable only with abraser. Excellent abrasive wear, moderate crashworthiness oxidation resistance, high heat resistance.

PURPOSE AND FIELD OF APPLICATION

Electrodes provide alloy martensitic steel in deposition. They are designed for deposition reinforcing layers, that work in conditions of abrasive wear with moderate dynamic loads. Electrodes are suitable for overlaying of agricultural implement, that work in moderate humidity conditions; woodworking tools, loaders.

APPLICATION CONDITIONS

It is recommended to carry an electrode vertically to detail. Deposition should be carried out with a short arc and the lowest possible current to prevent mixing with parent metal. To achieve maximum hardness on low-carbon steels it is necessary to conduct 3-layer surfacing.

 

 

REDRYING BEFORE WELDING

At the normal storage conditions, the redrying is not required. In case of moisture redrying is made at 350-370°С for 60 min. 3 times max.

 

CHEMICAL COMPOSITION OF DEPOSITED METAL, %

Mn C P S Cr Mo Nb
≤3.0 ≤2,5 ≤ 0.04 ≤ 0.04 ≤10 ≤3.0 ≤10

 

HARDNESS OF DEPOSITED METAL

52-58 HRС

Welding should be made at DC of reverse polarity «+» at the electrode.

PACKAGING DATA

Diameter, mm Length, mm Welding current, A Units per package, pcs Weight of packing, kg
2.5 350 70-100 52-53 1
3 350 80-120 30-31 1
3.2 350 90-130 27-28 1
4 450 110-170 14 1
5 450 140-200 9 1

 

WELDING POSITIONS