COATING TYPE — Graphite-basic
ТУ У 25.9-34142621-019:2019 |
ISO 1071: E С NiFe – Cl 3 |
AWS A5.15: E NiFe – CI |
SPECIAL PROPERTIES
The electrode provides a stable arc and minimal spatter. The deposited metal has high strength and hot cracks resistance. Therefore, this electrode is suitable for welding parts made of gray, malleable and high-strength cast iron, details operating at high loads.
APPLICATION CONDITIONS
The welding area must be cleaned. Welding is carried out without preheating, or with a slight heating. The beads should be welded only in the lateral direction without transverse oscillations of the electrode, no more than 50 mm of weld in one pass. In multi-layer surfacing, cool every layer in the air to a temperature of 60 ° C. after welding, immediately hammer the bead
REDRYING BEFORE WELDING
At the normal storage conditions, the redrying is not required. The moisture content of the electrode coating should not exceed 0.3% before use. In case of moisture redrying is made at 180-220°C 60 min
CHEMICAL COMPOSITION OF WELD METAL, %
C |
Mn |
Si |
S |
Ni |
Fe |
P |
0.8-1.5 |
1.0-2.5 |
≤ 1.0 |
≤ 0.03 |
≥52.0 |
≤ 45.0 |
≤ 0.03 |
MECHANICAL PROPERTIES OF WELD METAL
Tensile strength, MPa |
Elongation, % |
Hardness, НВ |
≥ 450 |
≥ 10 |
≥180 |
WELDING CONDITIONS
4125-145
Diameter, mm |
Welding current, A |
2.5 |
50-80 |
3.0 |
70-100 |
3.2 |
80-110 |
Welding should be made at DC of reverse polarity («+» on electrode ) or AC.
PACKAGING DATA
Diameter, mm |
Length, mm |
Number of electrodes in package, pc. |
Weight of packing, kg |
2.5 |
350 |
62-63 |
1 |
3.0 |
350 |
35-36 |
1 |
3.2 |
350 |
31-33 |
1 |