COATING TYPE - Rutile

AWS A 5.1:E 6013 ISO 2560-A-E 42 0 RC 11 ГОСТ 9466 - 75

Э 46 –Стандарт РЦ-Ø-УД

Е 43 2(3) РЦ 11

ТУ У 25.9-34142621-008:2012

Electrodes “Standart RC” have advanced formula that provides improved welding and technological properties, working from small (domestic) transformers, namely: easy primary ignition, forming small-scope metal joint, easy self-peeling slag. It is possible using for tacks, short and root welding beads at low voltage in a system.

PURPOSE AND FIELD OF APPLICATION

Electrodes “Standart RC” designed for manual metal arc welding of general and critical structures of carbon steels according to ДСТУ 2651 / ГОСТ 380 (Ст 0, Ст 1, Ст 2, Ст 3) of all disoxidation degrees – "Rimmed" (“КП”), "Semi-killed" (“ПС”), "Killed" (“СП”) and ГОСТ 1050 (05кп, 08кп, 08пс, 08, 10кп, 10пс, 10, 15кп, 15пс, 15, 20кп, 20пс, 20). 

APPLICATION CONDITIONS

Deposition rate factor – 8,5-9,5 g/А.hr. Electrode consumption per 1 kg of deposited metal is 1,7 kg. Electrodes “Standart RC” suitable for corner, butt and fillet joint types on metal with 3-20 mm thickness. Electrodes with diameter range from 2 to 4 mm applicable in all welding positions. Electrodes with diameter 5 mm can be used in horizontal flat, horizontal down hand, transverse and vertical up positions. Welding in vertical down position is carried out by short arc or deep-penetration method, herewith electrode must be in bisector flat area and the travel angle may vary 40 – 70°.

REDRYING BEFORE WELDING

At the normal storage conditions, redrying is not required. In case of moisture the redrying is made at 110±10°С for 40-60 min.

 

CHEMICAL COMPOSITION OF DEPOSITED METHAL, %

Mn Si C P S
0.40-0.75 0.15-0.35 ≤ 0.11 ≤ 0.035 ≤ 0.035

MECHANICAL PROPERTIES OF WELD METAL

Tensile strength, MPa Yield strength, MPa Elongation, %

Impact strength, J / cm²

+20 ˚С

Absorbed striking energy, J

0 ˚С

500-640 ≥ 420 ≥ 22 ≥ 78 ≥ 47

Welding should be done with DC of any polarity (reverse polarity is recommended, “+” on electrode) or with AC current from a transformer with open-circuit voltage not less than 50V.

 

 

PACKAGING DATA

Diameter, mm Length, mm Current, А Number of electrodes in a package, pc. Weight of packing, kg
2 300 40-90 101-107 1
2.5 350 50-100 54-57; 135-143 1;2.5
3 350 70-120 37-39; 92-96 1;2.5
3.2 350 80-130 32-34; 82-85 1;2.5
4 450 110-180 16-17; 42-44; 84-87 1;2.5; 5
5 450 150-230 27; 54-55 2,5; 5

WELDING POSITIONS

PA PB PC PF

 

PG PE PD

 

ДСТУ EN ISO 6947

 

 